YM201 cemented carbide cutting inserts, the equivalent of ISO grouping code K10. Density of 13.9g/cm ³, a bending strength of 1600MPa, hardness 93.0HRA. For cast iron, non-ferrous metal finishing, semi-finishing, can be used for manganese steel, hardened steel machining. YM201 coated cemented carbide cutting inserts having a low friction coefficient, can reduce the cutting force and the cutting temperature of the cutting, it can greatly improve the durability of the tool (YM201 coated cemented carbide cutting insert can improve a durability of at least X). Current common coating has been the first single TiC, TiN, Al2O3, developed to phase composite film, thick film, and multi-coating.
2014年6月18日星期三
YM201 Cemented Carbide Cutting Inserts Introduction
YM201 cemented carbide cutting inserts, the equivalent of ISO grouping code K10. Density of 13.9g/cm ³, a bending strength of 1600MPa, hardness 93.0HRA. For cast iron, non-ferrous metal finishing, semi-finishing, can be used for manganese steel, hardened steel machining. YM201 coated cemented carbide cutting inserts having a low friction coefficient, can reduce the cutting force and the cutting temperature of the cutting, it can greatly improve the durability of the tool (YM201 coated cemented carbide cutting insert can improve a durability of at least X). Current common coating has been the first single TiC, TiN, Al2O3, developed to phase composite film, thick film, and multi-coating.
订阅：
博文评论 (Atom)
没有评论:
发表评论