YG610 cemented carbide cutting insert, having a density of 14.60 ~ 14.80g/cm ³, flexural strength of not less than 2000 N / MM ², hardness of not less than 93.5HRA. Since YG610 cemented carbide cutting blade abrasion resistance, high red hardness, so YG610 carbide cutting blade is widely used in continuous or intermittent cutting cast iron, high temperature alloys, quenching and other materials. YG610 cemented carbide cutting inserts with the composition range of the WC / Co is about 2% -13% cobalt, and its small particulate size greater than 0.5 to 5μm (0.00002-0.0002 inches). The recent discovery of submicron (less than .00004 inches) and a relatively high fine carbide cobalt component combination of "fine particle" used in the carbide to increase the processing speed and under high rate processing.
2014年6月18日星期三
YG610 Cemented Carbide Cutting Inserts Introduction
YG610 cemented carbide cutting insert, having a density of 14.60 ~ 14.80g/cm ³, flexural strength of not less than 2000 N / MM ², hardness of not less than 93.5HRA. Since YG610 cemented carbide cutting blade abrasion resistance, high red hardness, so YG610 carbide cutting blade is widely used in continuous or intermittent cutting cast iron, high temperature alloys, quenching and other materials. YG610 cemented carbide cutting inserts with the composition range of the WC / Co is about 2% -13% cobalt, and its small particulate size greater than 0.5 to 5μm (0.00002-0.0002 inches). The recent discovery of submicron (less than .00004 inches) and a relatively high fine carbide cobalt component combination of "fine particle" used in the carbide to increase the processing speed and under high rate processing.
订阅：
博文评论 (Atom)
没有评论:
发表评论