YG6A cemented carbide cutting inserts, the equivalent of ISO grouping code K10. Its density is 14.7 ~ 15.1g/cm ³, bending strength of not less than 1420 N / MM ², hardness of not less than 91HRA. YG6A carbide cutting inserts its high hardness, flexural capacity suitable for hot and cold strong hard cast iron, alloy cast iron, heat-resistant steel, alloy steel processing, but also for ordinary cast iron finish. YG6A alloys are fine particles, abrasion resistance, suitable for chilled cast iron, nonferrous metals and alloys semi-finishing, but also for hardened steel, alloy steel, semi-finishing and finishing. Carbide is a refractory metal with high hardness carbide (WC, TiC) as a main component micron powder, cobalt (Co) or nickel (Ni), molybdenum (Mo) as a binder, in a vacuum or hydrogen furnace reduction furnace sintering powder metallurgy products.
2014年6月9日星期一
YG6A Cemented Carbide Cutting Inserts Introduction
YG6A cemented carbide cutting inserts, the equivalent of ISO grouping code K10. Its density is 14.7 ~ 15.1g/cm ³, bending strength of not less than 1420 N / MM ², hardness of not less than 91HRA. YG6A carbide cutting inserts its high hardness, flexural capacity suitable for hot and cold strong hard cast iron, alloy cast iron, heat-resistant steel, alloy steel processing, but also for ordinary cast iron finish. YG6A alloys are fine particles, abrasion resistance, suitable for chilled cast iron, nonferrous metals and alloys semi-finishing, but also for hardened steel, alloy steel, semi-finishing and finishing. Carbide is a refractory metal with high hardness carbide (WC, TiC) as a main component micron powder, cobalt (Co) or nickel (Ni), molybdenum (Mo) as a binder, in a vacuum or hydrogen furnace reduction furnace sintering powder metallurgy products.
订阅：
博文评论 (Atom)
没有评论:
发表评论