P10 Tungsten Carbide Bar Performance

P10 tungsten carbide bar strips density 11.0g / cm³ into 11.7g / cm³ range, the flexural strength of not less than 1150N / mm², hardness of not less than 91HRA. Mainly by a mix of tungsten carbide and cobalt powder metallurgy method by milling, ball milling, pressing, sintering, has good wear resistance and flexural strength. With WC amount within the range of 60% to 90%, the cobalt content is between 4% and 9%, titanium content is 8% to 20% plus or minus, containing tantalum content is 0% to 20% range. The main components of tungsten carbide and cobalt alloys, different uses ingredients of tungsten carbide long and cobalt are not consistent, the use of a very wide range. Alloy strip is one of a number of materials, predominantly in a stripe shape. 

P10 tungsten carbide bar strip production process is mainly carried out in accordance with the following steps: milling → ​​joined by end-use requirements by wet grinding recipe → mixed → crush → drying → sieving after forming agent → sieved and dried after the prepared mix → granulation → HIP pressing sintering → forming → low pressure molding (blank) detection test → packing → ​warehousing.