M10 tungsten carbide bar hardness of not less than 91.5HRA, density is about 14.9g/cm³. The main components of tungsten carbide and cobalt alloys, different uses ingredients of tungsten carbide long and cobalt are not consistent, the use of a very broad range. Flexural strength of not less than 1900MPa, the amount of tungsten carbide in the range of 78% to 94%, the cobalt content is between 4% and 9%, containing titanium in an amount from 3 to 11% plus or minus, tantalum content 0% to 11% range. Many long carbide is a material, primarily in a stripe shape. Mainly by the use of tungsten carbide and cobalt powder metallurgy method by mixing flour, milling, pressing, sintering, and has good abrasion resistance and flexural strength.
2014年8月7日星期四
M10 Tungsten Carbide Bar Feature
M10 tungsten carbide bar hardness of not less than 91.5HRA, density is about 14.9g/cm³. The main components of tungsten carbide and cobalt alloys, different uses ingredients of tungsten carbide long and cobalt are not consistent, the use of a very broad range. Flexural strength of not less than 1900MPa, the amount of tungsten carbide in the range of 78% to 94%, the cobalt content is between 4% and 9%, containing titanium in an amount from 3 to 11% plus or minus, tantalum content 0% to 11% range. Many long carbide is a material, primarily in a stripe shape. Mainly by the use of tungsten carbide and cobalt powder metallurgy method by mixing flour, milling, pressing, sintering, and has good abrasion resistance and flexural strength.
订阅：
博文评论 (Atom)
没有评论:
发表评论